Polyamide 6 grade 6 B300

Polyamide 6 grade 6 B300

Product Order

Product Order

Physical Properties
	value	unit	Test Conditions	Test Method
Density	1.14	g / cm³		ISO 1183
Moisture Content	0.14	WT.%		ISO 62
Mechanical properties
	value	unit	Test Conditions	Test Method
Hardness Shore D	72			ISO 868
Izod Impact, Notched	8.25	kJ / m²		ISO 180
Izod Impact, Unnotched	0	kJ / m²	0 = Not Break	ISO 180
Tensile Elongation at Break	78	%	5mm / min	ASTM D638
Tensile Modulus	7235.9	MPa	5mm / min	ASTM D638
Tensile Strength at Break	55.2	MPa	5mm / min	ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Heat Deflection Temperature	218.6	C °	At 1.8MPa, 120 ° C / hr	ASTM D648
Heat Deflection Temperature	91.3	C °	At 0.45MPa, 120 ° C / hr	ASTM D648
Vicat Softening Point	205.3	C °	At 10N, 50 ° C / h	ASTM D1525
Vicat Softening Point	172.3	C °	At 50N, 50 ° C / h	ASTM D1525

For this product no file has been considered.

Physical Properties
	value	unit	Test Conditions	Test Method
Density	1.14	g / cm³		ISO 1183
Moisture Content	0.14	WT.%		ISO 62
Mechanical properties
	value	unit	Test Conditions	Test Method
Hardness Shore D	72			ISO 868
Izod Impact, Notched	8.25	kJ / m²		ISO 180
Izod Impact, Unnotched	0	kJ / m²	0 = Not Break	ISO 180
Tensile Elongation at Break	78	%	5mm / min	ASTM D638
Tensile Modulus	7235.9	MPa	5mm / min	ASTM D638
Tensile Strength at Break	55.2	MPa	5mm / min	ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Heat Deflection Temperature	218.6	C °	At 1.8MPa, 120 ° C / hr	ASTM D648
Heat Deflection Temperature	91.3	C °	At 0.45MPa, 120 ° C / hr	ASTM D648
Vicat Softening Point	205.3	C °	At 10N, 50 ° C / h	ASTM D1525
Vicat Softening Point	172.3	C °	At 50N, 50 ° C / h	ASTM D1525