Polyamide 66 Grade 66 B100

Polyamide 66 Grade 66 B100

Product Order

Product Order

Physical Properties
	value	unit	Test Conditions	Test Method
Density	1.12	g / cm³		ISO 1183
Moisture Content	0.13	WT.%		ISO 62
Mechanical properties
	value	unit	Test Conditions	Test Method
Hardness Shore D	73			ISO 868
Izod Impact, Notched	5.12	kJ / m²		ISO 180
Izod Impact, Unnotched	0	kJ / m²	0 = Did Not Break	ISO 180
Tensile Elongation at Break	29.8	%	5mm / min	ASTM D638
Tensile Modulus	10802.5	MPa	5mm / min	ASTM D638
Tensile Strength at Break	68.8	MPa	5mm / min	ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Heat Deflection Temperature	231.2	C °	At 1.8MPa, 120 ° C / hr	ASTM D648
Vicat Softening Point	220.2	C °	At 0.45MPa, 120 ° C / hr	ASTM D648
Vicat Softening Point	255.6	C °	At 10N, 50 ° C / h	ASTM D1525
Vicat Softening Point	178.6	C °	At 50N, 50 ° C / h	ASTM D1525

For this product no file has been considered.

Physical Properties
	value	unit	Test Conditions	Test Method
Density	1.12	g / cm³		ISO 1183
Moisture Content	0.13	WT.%		ISO 62
Mechanical properties
	value	unit	Test Conditions	Test Method
Hardness Shore D	73			ISO 868
Izod Impact, Notched	5.12	kJ / m²		ISO 180
Izod Impact, Unnotched	0	kJ / m²	0 = Did Not Break	ISO 180
Tensile Elongation at Break	29.8	%	5mm / min	ASTM D638
Tensile Modulus	10802.5	MPa	5mm / min	ASTM D638
Tensile Strength at Break	68.8	MPa	5mm / min	ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Heat Deflection Temperature	231.2	C °	At 1.8MPa, 120 ° C / hr	ASTM D648
Vicat Softening Point	220.2	C °	At 0.45MPa, 120 ° C / hr	ASTM D648
Vicat Softening Point	255.6	C °	At 10N, 50 ° C / h	ASTM D1525
Vicat Softening Point	178.6	C °	At 50N, 50 ° C / h	ASTM D1525