Polycarbonate grade PGPC 0407

Product Order

Physical Properties
	value	unit	Test Conditions	Test Method
Density	1.2	g / cm³		ASTM D792
MFI	4.1 - 7	g / 10min	At 1.2Kg Load, 300 ° C	ASTM D1238
Mechanical properties
	value	unit	Test Conditions	Test Method
Charpy Impact Notched	25	kJ / m²		ASTM D256
Hardness Ball Indentation	103	MPa
Tensile Elongation at Break	100	%		ASTM D638
Tensile Modulus	2200 - 2400	MPa		ASTM D638
Tensile Strength at Yield	60	MPa		ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Vicat Softening Point	145 - 150	C °	At 50 N, 50 ° C / h	ASTM D1525
Electrical Properties
	value	unit	Test Conditions	Test Method
Dielectric Constant	2.8 - 3.1		At 1 MHz	ASTM D150
Dielectric Strength	20	kV / mm	At 50 HZ, 50mm diameter, 2mm thickness	ASTM D149
Dissipation factor	80 - 110	E-4	At 1 MHz	ASTM D150
Dissipation factor	8 - 10	E-4	At 50 MHz	ASTM D150
Optical properties
	value	unit	Test Conditions	Test Method
Transmission, Visible	80	%	Thickness 2 mm	ASTM D1003

For this product no file has been considered.

Physical Properties
	value	unit	Test Conditions	Test Method
Density	1.2	g / cm³		ASTM D792
MFI	4.1 - 7	g / 10min	At 1.2Kg Load, 300 ° C	ASTM D1238
Mechanical properties
	value	unit	Test Conditions	Test Method
Charpy Impact Notched	25	kJ / m²		ASTM D256
Hardness Ball Indentation	103	MPa
Tensile Elongation at Break	100	%		ASTM D638
Tensile Modulus	2200 - 2400	MPa		ASTM D638
Tensile Strength at Yield	60	MPa		ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Vicat Softening Point	145 - 150	C °	At 50 N, 50 ° C / h	ASTM D1525
Electrical Properties
	value	unit	Test Conditions	Test Method
Dielectric Constant	2.8 - 3.1		At 1 MHz	ASTM D150
Dielectric Strength	20	kV / mm	At 50 HZ, 50mm diameter, 2mm thickness	ASTM D149
Dissipation factor	80 - 110	E-4	At 1 MHz	ASTM D150
Dissipation factor	8 - 10	E-4	At 50 MHz	ASTM D150
Optical properties
	value	unit	Test Conditions	Test Method
Transmission, Visible	80	%	Thickness 2 mm	ASTM D1003