HP525J grade polypropylene homopolymer

HP525J grade polypropylene homopolymer

Product Order

Product Order

Physical Properties
	value	unit	Test Conditions	Test Method
Density	0.9	g / cm³		ASTM D1505
MFI	3	g / 10min	At 2.16Kg Load, 230 ° C	ASTM D1238
Mechanical properties
	value	unit	Test Conditions	Test Method
Flexural Modulus	1550	MPa		ASTM D790
Hardness, Rockwell R	105			ASTM D785
Izod Impact Strength, Notched	55	J / m	at + 23 ° C	ASTM D256
Tensile Elongation at Yield	12	%		ASTM D638
Tensile Strength at Yield	35	MPa		ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Heat Deflection Temperature	94	C °	At 0.46 MPa	ASTM D648
Oven Aging	500	h	Temperature 150 ° C	ASTM D3012
Vicat Softening Point	156	C °	10N	ASTM D1525
Optical properties
	value	unit	Test Conditions	Test Method
Haze	0.5	%	20µm	ASTM D1003

For this product no file has been considered.

Physical Properties
	value	unit	Test Conditions	Test Method
Density	0.9	g / cm³		ASTM D1505
MFI	3	g / 10min	At 2.16Kg Load, 230 ° C	ASTM D1238
Mechanical properties
	value	unit	Test Conditions	Test Method
Flexural Modulus	1550	MPa		ASTM D790
Hardness, Rockwell R	105			ASTM D785
Izod Impact Strength, Notched	55	J / m	at + 23 ° C	ASTM D256
Tensile Elongation at Yield	12	%		ASTM D638
Tensile Strength at Yield	35	MPa		ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Heat Deflection Temperature	94	C °	At 0.46 MPa	ASTM D648
Oven Aging	500	h	Temperature 150 ° C	ASTM D3012
Vicat Softening Point	156	C °	10N	ASTM D1525
Optical properties
	value	unit	Test Conditions	Test Method
Haze	0.5	%	20µm	ASTM D1003