LL0209AA Grade Light Line Polyethylene

Product Order

Physical Properties
	value	unit	Test Conditions	Test Method
Density	0.921	g / cm³		ASTM D1505
MFI	0.9	g / 10min	At 2.16Kg Load	ASTM D1238
Mechanical properties
	value	unit	Test Conditions	Test Method
Film Elongation at Break, MD	620	%		ASTM D882
Film Elongation at Break, TD	840	%		ASTM D882
Film Tensile Strength at Break, MD	41	MPa		ASTM D882
Film Tensile Strength at Break, TD	32	MPa		ASTM D882
Film Tensile Strength at Yield, MD	10	MPa		ASTM D882
Film Tensile Strength at Yield, TD	11	MPa		ASTM D882
Impact Strength, Dart	100	gr	Method A	ASTM D1709
Thermal properties
	value	unit	Test Conditions	Test Method
Vicat Softening Point	105	C °		ASTM D1525
Optical properties
	value	unit	Test Conditions	Test Method
Gloss	36		45 °	ASTM D2457
Haze	12	%		ASTM D1003

For this product no file has been considered.

Physical Properties
	value	unit	Test Conditions	Test Method
Density	0.921	g / cm³		ASTM D1505
MFI	0.9	g / 10min	At 2.16Kg Load	ASTM D1238
Mechanical properties
	value	unit	Test Conditions	Test Method
Film Elongation at Break, MD	620	%		ASTM D882
Film Elongation at Break, TD	840	%		ASTM D882
Film Tensile Strength at Break, MD	41	MPa		ASTM D882
Film Tensile Strength at Break, TD	32	MPa		ASTM D882
Film Tensile Strength at Yield, MD	10	MPa		ASTM D882
Film Tensile Strength at Yield, TD	11	MPa		ASTM D882
Impact Strength, Dart	100	gr	Method A	ASTM D1709
Thermal properties
	value	unit	Test Conditions	Test Method
Vicat Softening Point	105	C °		ASTM D1525
Optical properties
	value	unit	Test Conditions	Test Method
Gloss	36		45 °	ASTM D2457
Haze	12	%		ASTM D1003