RG 1101R grade polypropylene homopolymer

RG 1101R grade polypropylene homopolymer

Product Order

Product Order

Physical Properties
	value	unit	Test Conditions	Test Method
Density	0.91	g / cm³		ASTM D792
MFI	20	g / 10min	At 21.6Kg, 230 ° C	ASTM D1238
Mechanical properties
	value	unit	Test Conditions	Test Method
Charpy Impact Notched	2.5	kJ / m²	At 23 ° C	ISO 179 / 1eA
Charpy Impact Notched	1.5	kJ / m²	At -30 ° C	ISO 179 / 1eA
Hardness Ball Indentation	78	MPa		ISO 2039-1
Tensile Elongation at Yield	8	%	50mm / min	ASTM D638
Tensile Modulus	1500	MPa	1mm / min	ASTM D638
Tensile Strength at Yield	34	MPa	50mm / min	ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Heat Deflection Temperature	85	C °	At 0.46MPa	ASTM D648
Melting Point	163	C °	DSC Analysis	ASTM D3417
Vicat Softening Point	154	C °	10N	ASTM D1525

For this product no file has been considered.

Physical Properties
	value	unit	Test Conditions	Test Method
Density	0.91	g / cm³		ASTM D792
MFI	20	g / 10min	At 21.6Kg, 230 ° C	ASTM D1238
Mechanical properties
	value	unit	Test Conditions	Test Method
Charpy Impact Notched	2.5	kJ / m²	At 23 ° C	ISO 179 / 1eA
Charpy Impact Notched	1.5	kJ / m²	At -30 ° C	ISO 179 / 1eA
Hardness Ball Indentation	78	MPa		ISO 2039-1
Tensile Elongation at Yield	8	%	50mm / min	ASTM D638
Tensile Modulus	1500	MPa	1mm / min	ASTM D638
Tensile Strength at Yield	34	MPa	50mm / min	ASTM D638
Thermal properties
	value	unit	Test Conditions	Test Method
Heat Deflection Temperature	85	C °	At 0.46MPa	ASTM D648
Melting Point	163	C °	DSC Analysis	ASTM D3417
Vicat Softening Point	154	C °	10N	ASTM D1525